We focus on polyurethane for shoe sole

Low-hardness and medium-density shoe sole PU resin for casual shoes for both men and women ZG-P-8086D/ZG-I-9823D

ZG-P-8086/ZG-I-9823

Super high-hardness and super low-density PU Resin for shoe sole

Characteristic: Super-high hardness, super-low density.

Application: Applicable to the production of shoe soles for both men and women


Low-hardness and medium-density shoe sole PU resin for casual shoes for both men and women ZG-P-8086D/ZG-I-9823D


Typical properties of PU Resin

Name of productsAppearanceViscosity(Pa·s/50℃)Density(g/cm3/40℃)Package(kg)
ZG-P-8086White or pale yellow, liquid, no foreign material0.30-0.701.16-1.2018
ZG-I-9823Transparent liquid, no foreign material0.05-0.201.18-1.2020

Reference shipments ratio: A/B=28/25(barrel)


Catalysts and auxiliary agents

ZG-P-8086/ZG-AC-2/water =18kg/230g/70-120g

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.


Molding conditions & physical properties:

ReactivityTechnical indexTest itemReference physical properties
Reference ratioP+C/I100/98-102Molded density of sole(g/cm30.30~0.40
Using temperature(℃)material: 45-50; B material: 38-42Hardness (type A)75~80
Cream time(s)6~9Tensile strength(MPa)
Rise time(s)30~45Elongation(%)
Metal mold temperature(℃)55~65NBS abrasion resistance(%)≥10%
Demould time(min)5.0~7.0Free foam density(g/cm30.12~0.15


Folding endurance (room temperature)(40,000 gap length mm)


Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).

Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.