We focus on polyurethane for shoe sole

Low-hardness and medium-density shoe sole PU resin for casual shoes for both men and women ZG-P-7165/ZG-I-7249

ZG-P-7165/ZG-I-7249

Medium and low-hardness and medium and low-density PU Resin for sole of casual shoes for both men and women

Characteristic: Medium and low hardness, medium and  low density.

Application: Applicable to the production of medium soles of casual shoes for both men and women


Low-hardness and medium-density shoe sole PU resin for casual shoes for both men and women ZG-P-7165/ZG-I-7249


Typical properties of PU Resin

Name of productsAppearanceViscosity(Pa·s/50℃)Density(g/cm3/40℃)Package(kg)
ZG-P-7165White or pale yellow, liquid, no foreign material0.50-1.001.16-1.2018
ZG-I-7249Transparent liquid, no foreign material0.10-0.301.18-1.2020

Reference shipments ratio: A/B=30/23(barrel)


Catalysts and auxiliary agents:

ZG-P-7165/ZG-AC-2/water=18kg/220g/60-80g

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.


Molding conditions & physical properties:

ReactivityTechnical indexTest itemReference physical properties
比Reference ratioP+C/I100/87-89Molded density of sole(g/cm30.38~0.45
Using temperature(℃)material: 45-50; B material:38-42Hardness (type A)40~55
Cream time(s)6~9Tensile strength(MPa)3.5~4.5
Rise time(s)30~45Elongation(%)350~450
Metal mold temperature(℃)55~65NBS abrasion resistance(%)≥10%
Demould time(min)4.0~6.0Free foam density(g/cm30.15~0.18


Folding endurance (room temperature)(40,000 gap length mm)<8


Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).

Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.