We focus on polyurethane for shoe sole

Low-hardness and medium-density shoe sole PU resin for safety shoes for both men and women ZG-P-6570H/ZG-I-7118


PU Resin for shoe sole with the upper

Characteristic: Medium and low hardness, medium and high density

Application: Applicable to the production of shoe sole with the upper for men and women

Low-hardness and medium-density shoe sole PU resin for casual shoes for both men and women ZG-P-6570H/ZG-I-7118

Typical properties of PU Resin

Name of productsAppearanceViscosity(Pa·s/50℃)Density(g/cm3/40℃)Package(kg)
ZG-P-6570HWhite or pale yellow, liquid, no foreign material0.60-0.80------18
ZG-I-7118Transparent liquid, no foreign material0.20-0.40------20

Reference shipments ratio: A/B=29/24 (barrel)

Catalysts and auxiliary agents:

ZG-P-6570/ZG-AC-2/water =18kg/260g/10-35g/0~400g

Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.

Molding conditions & physical properties:

ReactivityTechnical indexTest itemReference physical properties
Reference ratioP+C/I100/68-70Molded density of sole(g/cm30.70~1.10
Material temperature(℃)material: 45-50; B material:38-42Hardness (type A)55~65
Cream time(s)6~9Tensile strength(MPa)5.0~7.0
Rise time(s)30~45Elongation(%)350~450
Metal mold temperature(℃)45~55NBS abrasion resistance(%)≥10%
Demould time(min)3.0~5.0Free foam density(g/cm30.25~0.30

Folding endurance (room temperature) (40,000 gap length mm)


Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.

Free foam density will vary with the seasons (temperature, humidity).

Stripping time will be extended with the increase of the thickness of moldings.

Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times

Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.